C95800
| Elements | |||||||
|---|---|---|---|---|---|---|---|
| Cu(1) | Pb | Fe(2) | Ni(3) | Al | Mn | Si | |
|
(1) Cu + Sum of Named Elements 99.5% min. (2) Fe content shall not exceed Ni content. (3) Fe content shall not exceed Ni content. |
|||||||
| Min (%) | 79.0 | 3.5 | 4.0 | 8.5 | 0.8 | ||
| Max (%) | 0.03 | 4.5 | 5.0 | 9.5 | 1.5 | 0.10 | |
| Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell B scale | Brinell Hardness, 3000 kg load | Shear Strength (ksi) |
Izod (ft-lbs) |
Charpy V-Notch Impact Strength (ft-lbs) |
Compressive Strength .001 in. set/in. (ksi) |
Compressive Strength .01 in. set/in. (ksi) |
Compressive Strength .1 in. set/in. (ksi) |
Fatigue Strength** (ksi) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| * Measured at room temperature, 68°F (20°C). ** Fatigue Strength: 100 x 106 cycles, unless indicated as [N] x 106. | ||||||||||||||
| As Centrifugal Cast | As Centrifugal Cast | M02 |
85 Min for Standard 85 Min for Standard |
35 Min for Standard |
15 Min for Standard 15 Min for Standard |
|||||||||
| As Continuous Cast | As Continuous Cast | M07 |
85 Min for Standard 85 Min for Standard |
35 Min for Standard |
18 Min for Standard 18 Min for Standard |
|||||||||
| As Permanent Mold Cast | As Permanent Mold Cast | M05 |
90 Min for Standard 96 Typ |
40 Min for Standard 52 Typ |
15 Min for Standard 17 Typ |
88 Typ |
||||||||
| As Sand Cast | As Sand Cast | M01 |
85 Min for Standard 85 Min for Standard 95 Typ |
35 Min for Standard 38 Typ |
15 Min for Standard 15 Min for Standard 25 Typ |
159 Typ |
58 Typ |
20 Typ | 16 Typ |
35 Typ | 48 Typ | 100 Typ | 31 Typ | |
| (1)Field Sterength 16 kA/m | |
| Melting Point - Liquidus°F | 1940 |
|---|---|
| Melting Point - Solidus°F | 1910 |
| Densitylb/cu in. at 68°F | 0.276 |
| Specific Gravity | 7.64 |
| Electrical Conductivity% IACS at 68°F | 7 |
| Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 20.8 |
| Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9 |
| Specific Heat CapacityBtu/ lb /°F at 68°F | 0.105 |
| Modulus of Elasticity in Tensionksi | 16500 |
| Magnetic Permeability | 1.05 (1) |
| Poisson's Ratio | 0.32 |
| Casting Attribute | Level |
|---|---|
| Casting Yield | Low |
| Drossing | High |
| Effect of Section Size | Low |
| Fluidity | Medium |
| Gassing | Medium |
| Patternmakers Shrinkage inches per inch | 3/16 |
| Shrinkage in Solidification | High |
| Technique | Suitability |
|---|---|
| Soldering | Good |
| Brazing | Fair |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Good |
| Machinability Rating | 20 |
Common Fabrication Processes
No fabrication process properties for this alloy
| Treatment | Value* | Time** | ||
|---|---|---|---|---|
| * Temperature is measured in Fahrenheit. ** Time is measured in minutes. | ||||
| Stress Relief | 600 | |||
| Solution Treatment | 0 | |||
| Product Category | Product | Reason Category | Reason |
|---|---|---|---|
| Fasteners | Nuts | Corrosion Resistance | Corrosion Resistance (Excellent) |
| Nuts | Machining Properties | Machinability, Good | |
| Nuts | Mechanical Properties | High Strength | |
| Industrial | Bushings | Corrosion Resistance | Corrosion Resistance (Excellent) |
| Bushings | Friction & Wear Properties | Wear Resistance | |
| Bushings | Machining Properties | Machinability, Good | |
| Bushings | Mechanical Properties | High Strength | |
| Gears | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Gears | Friction & Wear Properties | Wear Resistance | |
| Gears | Machining Properties | Machinability, Good | |
| Gears | Mechanical Properties | High Strength | |
| Machinery | Conductivity (Thermal) | Thermal Conductivity | |
| Machinery | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Machinery | Friction & Wear Properties | Wear Resistance | |
| Machinery | Mechanical Properties | High Strength | |
| Pickling Equipment | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Pickling Equipment | Corrosion Resistance | Corrosion Resistance to Acids | |
| Pickling Equipment | Mechanical Properties | High Strength | |
| Propeller Blades | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Propeller Blades | Friction & Wear Properties | Wear Resistance | |
| Propeller Blades | Mechanical Properties | Fatigue Strength | |
| Propeller Blades | Mechanical Properties | High Strength | |
| Propeller Hub | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Propeller Hub | Friction & Wear Properties | Wear Resistance | |
| Propeller Hub | Mechanical Properties | Fatigue Strength | |
| Propeller Hub | Mechanical Properties | High Strength | |
| Shafts | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Shafts | Friction & Wear Properties | Wear Resistance | |
| Shafts | Mechanical Properties | High Strength | |
| Valve Bodies | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Valve Bodies | Friction & Wear Properties | Wear Resistance | |
| Valve Bodies | Mechanical Properties | High Strength | |
| Wear Plates | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Wear Plates | Friction & Wear Properties | Wear Resistance | |
| Wear Plates | Mechanical Properties | High Strength | |
| Worm Wheels | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Worm Wheels | Friction & Wear Properties | Wear Resistance | |
| Worm Wheels | Machining Properties | Machinability, Good | |
| Worm Wheels | Mechanical Properties | High Strength | |
| Worms | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Worms | Friction & Wear Properties | Wear Resistance | |
| Worms | Mechanical Properties | High Strength | |
| Marine | Covers for Marine Hardware | Appearance | Appearance |
| Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
| Covers for Marine Hardware | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Covers for Marine Hardware | Mechanical Properties | High Strength | |
| Marine Hardware | Appearance | Appearance | |
| Marine Hardware | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Marine Hardware | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
| Marine Hardware | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
| Marine Hardware | Mechanical Properties | High Strength | |
| Ship Building | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Ship Building | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
| Ship Building | Corrosion Resistance | Corrosion Resistance to Salt Water | |
| Ship Building | Friction & Wear Properties | Wear Resistance | |
| Ship Building | Mechanical Properties | High Strength | |
| Valves in contact with sea water. | Corrosion Resistance | Corrosion Resistance (Excellent) | |
| Valves in contact with sea water. | Corrosion Resistance | Corrosion Resistance to Fresh Water | |
| Valves in contact with sea water. | Corrosion Resistance | Corrosion Resistance to Saline Solutions | |
| Valves in contact with sea water. | Friction & Wear Properties | Wear Resistance | |
| Valves in contact with sea water. | Mechanical Properties | High Strength | |
| Plumbing | Elbows | Corrosion Resistance | Corrosion Resistance (Excellent) |
| Elbows | Machining Properties | Machinability, Good | |
| Elbows | Mechanical Properties | High Strength | |
| Elbows | Mechanical Properties | Retains Strength at Elevated Temperatures |
| Form | Specific Sub-Form | Application | System | Standard | Description |
|---|---|---|---|---|---|
| As Centrifugal Cast | Castings | ASTM | B271/B271M | COPPER BASE ALLOY CENTRIFUGAL CASTINGS | |
| Castings | SAE | J462 | CAST COPPER ALLOYS | ||
| Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | ||
| As Continuous Cast | Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |
| Castings | SAE | J462 | CAST COPPER ALLOYS | ||
| Castings | ASTM | B505/B505M | COPPER BASE ALLOY CONTINUOUS CASTINGS | ||
| As Sand Cast | Castings | SAE | J461 | WROUGHT AND CAST COPPER ALLOYS | |
| Castings | SAE | J462 | CAST COPPER ALLOYS | ||
| Castings | ASTM | B148 | ALUMINUM BRONZE SAND CASTINGS | ||
| Castings | MILITARY | MIL-B-24480 | BRONZE, NICKEL-ALUMINUM CASTINGS, FOR SEAWATER SERVICE | ||
| Castings | ASTM | B763/B763M | COPPER ALLOY SAND CASTINGS FOR VALVE APPLICATIONS | ||
| Ingot | |||||
| ASTM | B30 | COPPER BASE ALLOYS IN INGOT FORM | |||
| Precision Cast | Castings | ASTM | B806 | PERMANENT MOLD CASTINGS | |
| Valves |
Corrosion Properties
No Corrosion Properties Available.