C96300
Elements | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|
Cu(1) | Pb | Fe | P | Ni(2) | C | Mn | S | Si | Nb | |
(1) Cu + Sum of Named Elements 99.5% min. (2) Ni value includes Co. |
||||||||||
Min (%) | 0.50 | 18.0 | 0.25 | 0.50 | ||||||
Max (%) | Rem | 0.01 | 1.5 | 0.02 | 22.0 | 0.15 | 1.5 | 0.02 | 0.50 | 1.5 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Brinell Hardness, 500 kg load |
---|---|---|---|---|---|---|
* Measured at room temperature, 68°F (20°C). | ||||||
As Sand Cast | As Sand Cast | M01 |
75 Typ |
55 Typ |
10 Typ |
150 Typ |
Melting Point - Liquidus°F | 2190 |
---|---|
Melting Point - Solidus°F | 2100 |
Densitylb/cu in. at 68°F | 0.323 |
Specific Gravity | 8.94 |
Electrical Conductivity% IACS at 68°F | 6 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 21.3 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 9.1 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 20000 |
Casting Attribute | Level |
---|---|
Casting Yield | Low |
Drossing | High |
Fluidity | Medium |
Gassing | Medium |
Shrinkage in Solidification | High |
Technique | Suitability |
---|---|
Soldering | Excellent |
Brazing | Excellent |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Fair |
Machinability Rating | 15 |
Common Fabrication Processes
Treatment | Time** | |||
---|---|---|---|---|
** Time is measured in minutes. | ||||
Solution Treatment | 0 |
Product Category | Product | Reason Category | Reason |
---|---|---|---|
Industrial | Tail shaft Sleeve | Corrosion Resistance | Corrosion Resistance |
Tail shaft Sleeve | Corrosion Resistance | Resists Erosion and Impingement Corrosion | |
Tail shaft Sleeve | Mechanical Properties | High Strength | |
Tail shaft Sleeve | Mechanical Properties | Retains Strength at Elevated Temperatures |
Applicable Specifications
Corrosion Properties